Abstract
This document describes a flexural, non-resonance method for determining the components of the flexural complex modulus Ef* of polymers at frequencies typically in the range 0,01 Hz to 100 Hz. Higher-frequency measurements can be made, but significant errors in the dynamic properties measured are likely to result (see 10.2.2 and 10.2.3). The method is suitable for measuring dynamic storage moduli in the range 10 MPa to 200 GPa.
NOTE Although materials with moduli less than 10 MPa can be studied, more accurate measurements of their dynamic-mechanical properties can be made using shear modes of deformation (see ISO 6721-6).
This method is particularly suited to the measurement of loss factors greater than 0,02 and can therefore be conveniently used to study the variation of dynamic properties with temperature and frequency through most of the glass-rubber relaxation region (see ISO 6721‑1). The availability of data determined over wide ranges of both frequency and temperature enables master plots to be derived, using frequency/temperature shift procedures, which present dynamic properties over an extended frequency range at different temperatures.
Read sample
General information
-
Status: PublishedPublication date: 2019-04Stage: International Standard under systematic review [90.20]
-
Edition: 2Number of pages: 11
-
Technical Committee :ISO/TC 61/SC 5ICS :83.080.01
- RSS updates
Life cycle
-
Previously
WithdrawnISO 6721-5:1996
WithdrawnISO 6721-5:1996/Amd 1:2007
-
Now
Got a question?
Check out our FAQs
Opening hours:
Monday to Friday - 09:00-12:00, 14:00-17:00 (UTC+1)