ISO 9327-2:1999
Steel forgings and rolled or forged bars for pressure purposes — Technical delivery conditions — Part 2: Non-alloy and alloy (Mo, Cr and CrMo) steels with specified elevated temperature properties
Reference number
ISO 9327-2:1999
Edition 1
1999-06
International Standard
Read sample
ISO 9327-2:1999
16995
Published (Edition 1, 1999)
This standard was last reviewed and confirmed in 2013. Therefore this version remains current.

ISO 9327-2:1999

ISO 9327-2:1999
16995
Language
Format
CHF 63
Convert Swiss francs (CHF) to your currency

Abstract

1.1 This part of ISO 9327 applies to forgings and rolled or forged bars in thicknesses up to 250 mm (partly up to

500 mm) manufactured from the steels listed in Table 1 and to be delivered according to the specifications given in

ISO 9327-1.

1.2 This part of ISO 9327 covers the following data:

a) in Table 1 the limits for

the chemical composition according to the cast analysis;

the tensile properties at room temperature;

the impact properties;

the indications on the usual heat treatment condition at the time of delivery;

b) in Table 2 the permissible product analysis tolerances on the limiting values given for the cast analysis;

c) in Table 3 the minimum elevated temperature proof strength values (see C.4 of ISO 9327-1:1998);

d) in Table 4 the estimated average stress rupture properties;

e) in Table 5 the estimated average strength values for 1 % plastic strain.

General information

  •  : Published
     : 1999-06
    : International Standard to be revised [90.92]
  •  : 1
     : 10